Effect of corrosion behavior on mechanical properties of steel under local failure mode of anti-corrosion coating
更新时间：2025-04-28

    • Effect of corrosion behavior on mechanical properties of steel under local failure mode of anti-corrosion coating

    • “Progress has been made in the study of the corrosion behavior of Q355B steel and its impact on mechanical properties under the failure mode of anti-corrosion coating, providing a solution to the problem of steel corrosion.”
    • Journal of Civil and Environmental Engineering   Pages: 1-12(2025)

    • DOI：10.11835/j.issn.2096-6717.2025.039    

      CLC： TU511.3

    • Received：07 November 2024，

      Online First：28 April 2025，

    移动端阅览

  • NIU Kai,ZHANG Liang,XU Weihao,et al.Effect of corrosion behavior on mechanical properties of steel under local failure mode of anti-corrosion coating[J].Journal of Civil and Environmental Engineering, DOI：10.11835/j.issn.2096-6717.2025.039.

  •  
  •  

0

Views

1

下载量

0

CSCD

Alert me when the article has been cited
提交
Tools
Download
Export Citation
Share
Add to favorites
Add to my album

Related Articles

State-of-the-art research and prospect of geopolymer solidified soil
Planting performance and durability of eco-concrete for slope protection
Experimental investigation on behavior of ultra-high performance concrete after high temperature
Mechanical and deformation properties of steel bars based on uniform/non-uniform corrosion characteristic parameters
Model experimental analysis of mechanical response process of buried polyethylene pipeline under the stacking load

Related Author

JIANG Bo
SU Yonghua
ZHANG Benben
LUO Zhengdong
LI Zhengyang
WANG Jiaqing
WU Jiansheng
HUANG Kaijian

Related Institution

College of Civil Engineering and Mechanics, Xiangtan University
College of Civil Engineering, Hunan University
College of Civil Engineering, Nanjing Forestry University
China Coal Science and Engineering Group Nanjing Design & Research Institute Co., Ltd.
School of Civil Engineering and Geomaticsm, Southwest Petroleum University
0